Cholesterol ester clathrate, water-holding composition, hydrous compositions, cosmetics containing the same, and processes for the preparation thereof

ABSTRACT

A cholesterol ester clathrate comprising a cholesterol ester included within a hydroxyalkylated cyclodextrin; a hydrous composition comprising a hydroxyalkylated cyclodextrin, a cholesterol ester and water; a hydrous composition comprising a hydroxyalkylated cyclodextrin, a cholesterol ester, a hydrous stabilizer, and water; a hydrous composition comprising a hydroxyalkylated cyclodextrin, a cholesterol ester, a clay mineral, and water; a cosmetic containing a hydrous composition; and processes for making the cholesterol ester clathrate and various hydrous compositions. The cholesterol ester clathrate exhibits an emulsifying effect and the hydrous compositions are excellent in water-holding capacity, hydration properties, and separation stability at a high temperature.

This application is a 371 of PCT/JP96/01815 filed Jul. 1, 1996.

TECHNICAL FIELD!

The present invention relates to cholesterol ester clathrate and hydrouscomposition comprising thereof and more particular, relates to theimprovement of the stability in hydrating and emulsifying said hydrouscomposition.

BACKGROUND ART!

Water-holding in skin is an essential factor for keeping the skin ingood condition. So, a lot of cosmetics and pharmaceutical preparationswhich intend the moisturizing are sold in the market, and a lot ofhumectants are developed. Among of these, a hydrous oily component,e.g., cholesterol ester which is excellent in hydration property andmoisturizing property, are used in particularly cosmetics.

However, in case of compounding such a hydrous oily component which wasincluded a lot of water to the cosmetics, it had some problems instability, since water was separated at a high temperature ortemperature change with the passage of time.

Therefore, for keeping the stability of the cosmetics which comprisingoil and water, various surfactants has been used in separately or bycombining two or more as an emulsifier.

However, ionic surfactants such as alkyl sulfate and higher fatty acidsalt has an apprehension of skin irritation, in the case where they areused at high concentration. And in case of using nonionic surfactantssuch as polyoxyethylene type, it has a problem in solubility such thatnonionic surfactants inactivate an antiseptic such as paraben.

In order to solve these problems, it has been developed techniques whichuses cyclodextrin or its derivatives as an emulsifier. Namely, JapaneseUnexamined Patent Publication No. Sho 58-58139 discloses the techniqueof emulsification by the specific process that cyclodextrin is used bycombination with oil soluble surfactant. Also, Japanese UnexaminedPatent Publication No. Sho 63-194726 discloses the technique which isused methylated β-cyclodextrin as an assistant emulsifier.

However, the problems such as skin irritation has not solved completely,since conventional surfactants are used by combining in thesetechniques.

In order to solve these problems, as for the example which is obtainedthe emulsion cosmetics without using any surfactant, the content inJapanese Unexamined Patent Publication No. Hei 3-284611 is listed.Namely, in Japanese Unexamined Patent Publication No. Hei 3-284611, theemulsion cosmetics which comprising a hydroxyalkylated cyclodextrin, oiland water is mentioned. This emulsion cosmetics is rich in solubilityand excellent in stability and safety.

However, such a cosmetics is still insufficient in the water-holdingcapacity for keeping the moisture, so it is desired the furtherimprovement.

Thereupon, it has been developed the techniques used a hydroxyalkylatedcyclodcxtrin which is effectively functioned to the composition as ahydrous stabilizer at the same time as an emulsifier.

However, in the water-holding of lipstick, and the like by using thesetechniques, the water-holding under the severe conditions such that isleft for a long period of time and at 90° C. in the preparation time, isstill insufficient. It sometimes occurs the aggregation of coloringagent and separate into a water phase and an oil phase or an emulsionphase, it is desired the further improvement.

DISCLOSURE OF INVENTION!

In view of the above-mentioned problems of the prior art, the object ofthe present invention is to provide a cholesterol clathrate which has anexcellent stability, safety and high water-holding capacity for keepingthe moisture, and has an emulsifying effect in itself, and is to providea hydrous composition which has an excellent stability, safety and highhydrous capacity for keeping the moisture, and has extremely excellenteffect which is not separated even under the severe condition such ashigh temperature.

As the result of diligent studies of the inventors for attaining theabove-mentioned object, it has been found that cholesterol esterclathrate comprising a cholesterol ester included in a hydroxyalkylatedcyclodextrin can be functioned as an excellent emulsifier by hydrophilicnature of cyclodextrin and lipophilic nature of cholesterol ester. And,in case of compounding the composition which comprising said cholesterolclathrate and water into the cosmetics and the like, it also has beenfound that the cosmetics which is excellent in stability and safety, andhas the specific property which is rich in water-holding capacity forkeeping the moisture can be obtained. Further, it also has been foundthat the compositions which comprising a hydroxyalkylated cyclodextrin,water, and a hydrous stabilizer has extremely high hydration properties,and the compositions which comprising a hydroxyalkylated cyclodextrin, acholesterol ester, water, and a clay mineral can be improved theseparation stability at high temperature. Accordingly, the presentinvention has been accomplished.

Namely, in a first aspect of the present invention, there is provided acholesterol ester clathrate comprising a cholesterol ester included in ahydroxyalkylated cyclodextrin.

In a second aspect of the present invention, there is provided a hydrouscomposition comprising a hydroxyalkylated cyclodextrin, a cholesterolester and water.

In said hydrous composition, preferably, the hydrous composition iscomposed of water and the cholesterol ester clathrate which is formed bythe hydroxyalkylated cyclodextrin and the cholesterol ester.

Also, in said hydrous composition, preferably, said compositioncomprises 5 to 30% by weight of the hydroxyalkylated cyclodextrin, 5 to80% by weight of the cholesterol ester, and 5 to 60% by weight of water.

Further, in said hydrous composition, preferably, the ratio of thecompounding amount of the hydroxyalkylated cyclodextrin and thecholesterol ester is existed within the range represented by the slantline of the triangular diagram shown in FIG. 1.

In a third aspect of the present invention, there is provided a hydrouscomposition comprising a hydroxyalkylated cyclodextrin, water, and oneor more of a hydrous stabilizer which is/are selected from the groupsuch as alkylated polysiloxane polyethyleneglycol copolymer, alkylsilicated anhydrous silicate, alkyl-modified silicone resin coatedpowder, glyceryl-modified silicone resin coated powder, dextrin fattyacid ester.

In said hydrous composition, preferably, said hydrous compositionfurther comprising a hydrous oily component.

Also, in said hydrous composition, preferably, said compositioncomprises 5 to 30% by weight of the hydroxyalkylated cyclodextrin, 5 to60% by weight of water and 5 to 80% by weight of the hydrous oilycomponent with respect to the whole amount of the hydrous composition.

Further, in said hydrous composition, preferably, the ratio of thecompounding amount of the hydroxyalkylated cyclodextrin, water and thehydrous oily component is existed within the range represented by theslant line of the triangular diagram shown in FIG. 2.

In said hydrous composition, it is preferable to comprise 0.01 to 20% byweight of the hydrous stabilizer with respect to the whole amount of thehydrous composition.

Preferably, alkylated polysiloxane polyethyleneglycol copolymer is usedas the hydrous stabilizer.

In a fourth aspect of the present invention, there is provided a hydrouscomposition which comprising a hydroxyalkylated cyclodextrin, acholesterol ester, a clay mineral and water.

In said hydrous composition, preferably, said composition comprises 5 to30% by weight of the hydroxyalkylated cyclodextrin, 5 to 80% by weightof the cholesterol ester, 0.01 to 20% by weight of the clay mineral, and5 to 60% by weight of water with respect to the whole amount of thehydrous composition.

In said hydrous composition, preferably, the clay mineral is a swellingtype clay mineral or an organophilic smectite, and in particular,synthetic sodium magnesium silicate is most preferable.

Further, in said hydrous composition, preferably, said compositionfurther comprising hydrophobic silica.

In said hydrous composition, preferably, said composition comprises 0.01to 20% by weight of hydrophobic silica with respect to the whole amountof the hydrous composition.

Also, in said hydrous composition, preferably, the ratio of thecompounding amount of hydrophobic silica to the clay mineral is 2:1 to1:4.

In a fifth aspect of the present invention, there is provided acosmetics comprising a hydroxyalkylated cyclodextrin, a cholesterolester and water.

In said cosmetics, preferably, a hydroxyalkylated cyclodextrin, acholesterol ester and water are compounded as any one of said hydrouscomposition.

And, in said cosmetics, preferably, the emulsion type of the cosmeticsis water-in-oil type.

Also, in said cosmetics, preferably, any one of said hydrous compositionis compounded with 0.5 to 30% by weight with respect to the whole amountof the cosmetics.

In a sixth aspect of the present invention, there is provided a processfor the preparation of a cholesterol ester clathrate which is obtainedby stirring and mixing a hydroxyalkylated cyclodextrin and a cholesterolester.

In a seventh aspect of the present invention, there is provided aprocess for the preparation of a hydrous composition which is obtainedby stirring and mixing a hydroxyalkylated cyclodextrin, water, and, acholesterol ester.

A process for the preparation of a hydrous composition which is obtainedby stirring and mixing the cholesterol ester clathiate which is preparedby the process for the preparation of the hydrous composition, andwater.

In said process for the preparation of the hydrous composition,preferably, 5 to 30% by weight of the hydroxyalkylated cyclodextrin, 5to 80% by weight of the cholesterol ester, 5 to 60% by weight of waterare compounded.

In said process for the preparation of the hydrous composition,preferably, the ratio of the compounding amount of the hydroxyalkylatedcyclodextrin and the cholesterol ester is existed within the rangerepresented by the slant line of the triangular diagram shown in FIG. 1.

In a eighth aspect of the present invention, there is provided a processfor the preparation of the hydrous composition which is obtained bystirring and mixing a hydioxyalkylated cyclodextrin; water; one or moreof a hydrous stabilizer which is/are selected from the group such asalkylated polysiloxane polycthyleneglycol copolymer, alkyl silicatedanhydrous silicate, alkyl-modified silicone resin coated powder,glyceryl-modified silicone resin coated powder and dextrin fatty acidester; and a hydrous oily component.

In said process for the preparation of the hydrous composition,preferably, 5 to 30% by weight of the hydroxyalkylated cyclodextrin, 5to 60% by weight of water, and 5 to 80% by weight of the hydrous oilycomponent are compounded with respect to the whole amount of the hydrouscomposition.

In said process for the preparation of the hydrous composition,preferably, the ratio of the compounding amount of the hydroxyalkylatedcyclodextrin, water, and the hydrous oily component is existed withinthe range represented by the slant line of the triangular diagram shownin FIG. 2.

In said process for the preparation of the hydrous composition,preferably, 0.01 to 20% by weight of the hydrous stabilizer iscompounded with respect to the whole amount of the hydrous composition.

Preferably, alkylated polysiloxane polyethyleneglycol copolymer is usedas the hydrous stabilizer.

In a ninth aspect of the present invention, there is provided a processfor the preparation of the hydrous composition which is obtained bystirring and mixing a hydroxyalkylated cyclodextrin, a cholesterolester, a clay mineral, and water.

In said process for the preparation of the hydrous composition,preferably, 5 to 30% by weight of the hydroxy alkylated cyclodextrin, 5to 80% by weight of the cholesterol ester, 0.01 to 20% by weight of theclay mineral, and 5 to 60% by weight of water are compounded withrespect to the whole amount of the hydrous composition.

Also, in said process for the preparation of the hydrous composition,the clay mineral is a swelling type clay mineral or an organophilicsmectite, and in particular, synthetic sodium magnesium silicate is mostpreferable.

Further, in said process for the preparation of the hydrous composition,preferably, the hydrous composition is obtained by compoundinghydrophobic silica, and stirring and mixing it.

In said process for the preparation of the hydrous composition,preferably, 0.01 to 20% by weight of hydrophobic silica is compounded.

Also, in said process for the preparation of the hydrous composition,preferably, the ratio of the compounding amount of hydrophobic silica tothe clay mineral is 2:1 to 1:4.

In a tenth aspect of the present invention, there is provided a processfor the preparation of the cosmetics which is obtained by stirring andmixing the hydrous composition which is prepared by any one of saidprocess for the preparation of the hydrous composition and otheringredients.

In said process for the preparation of the cosmetics, preferably, 0.5 Lo30% by weight of the hydrous composition which is prepared by any one ofsaid process for the preparation of the hydrous composition, iscompounded with respect to the whole amount of the cosmetics.

In the following, the constitutions of the present invention will beexplained in further detail.

<Constituents>

Hydroxyalkylated Cyclodextrin

A hydroxyalkylated cyclodextrin (hereinafter, referred to as HACD) usedin the present invention is the preparation which includes ahydroxyalkyl group into a hydroxyl group of cyclodextrin (hereinafter,referred to as CD) which is well known as cyclic oligosaccharide inconventional. Namely, the preparation includes the hydroxyalkyl groupwhich has hydrophobic nature, into the hydroxyl group of CD, and therebyits hydrophobic nature is enlarged.

The CD is oligosaccharide that a glucose residue is linked cyclically byα-1, 4-linkage, and α-CD, β-CD, and γ-CD which is comprised of a glucoseresidue of 6, 7, and 8 respectively are known in general. In the presentinvention, one or more of these CD can use by selecting.

As for the hydroxyalkyl group which substitute for the hydroxyl group ofCD, a hydroxyethyl group, a hydroxypropyl group and the like are mainlyused. The HACD can be obtained by doing substitution reaction of thesehydroxyalkyl groups and the hydroxyl group. Examples of the HACD includehydroxyethylated cyclodextrin, hydroxypropylated cyclodextrin,hydroxybutylated cyclodextrin, dihydroxypropylated cyclodextrin and thelike.

The preferable degree of substitution of a hydroxyl group and ahydroxyalkyl group in the present invention is 1 to 14 per CD.

Among of these HACD, in considering the price, easiness of preparation,usability, and water solubility, hydroxyethyl β-CD or hydroxypropyl β-CDis preferable. However, the HACD of the present invention is not limitedto these.

The process for the preparation of the HACD is known several process inconventional, it will be shown one example in the following.

Namely, dissolved 100 g of β-CD into 150 ml of 20% NaOH water solution,and gradually dropped 50 ml of propylene oxide under keeping at 30° C.,and then the reaction was keeping under stirring 20 hours. After the endof the reaction, neutralized it pH 6.0 by hydrochloric acid and put itinto permeable membrane tube, and then it was desalted under flowingwater in 24 hours. After then, dry it by freezing drying machine, andabout 90 g of hydroxypropyl β-CD was obtained. The degree ofsubstitution of this hydroxypropyl β-CD per CD was 5.1.

Hydrous Oily Component

Examples of a hydrous oily component used in the present inventioninclude a cholesterol ester.

Examples of the cholesterol ester as the hydrous oily component of thepresent invention include cholesterol and esters of higher fatty acid.As for the higher fatty acids, straight chain or branched chain fattyacid having a carbon number from 12 to 24 can be used, e.g., myristicacid, palmitic acid, palmitoleic acid, stearic acid, oleic acid,linoleic acid, linolenic acid, arachidic acid and the like are included.In the present invention, it is used by selecting from one or more ofthese higher fatty acids. As for the higher fatty acid which constitutethe ester with cholesterol used in the present invention, stearic acid,oleic acid, palmitoleic acid, macadamia nut oil fatty acid areparticularly preferable.

As for the cholesterol esters used in the present invention, cholesterolstearate, cholesterol oleate, cholesterol palmitate, cholesteryl esterof macadamia nut oil fatty acid are particularly preferable.

Hydrous Stabilizer

In the present invention, examples of a hydrous stabilizer includealkylated polysiloxane polyethyleneglycol copolymer, alkyl silicatedanhydrous silicate, alkyl-modified silicone resin coated powder,glyceryl-modified silicone resin coated powder, dextrin fatty acidester, and it is used by selecting one or more of these. All of thesesubstances are low in both hydrophilic nature and lipophilic nature, itis thinkable that they may be existed on the boundary of water and oilycomponent in membranous state. Among of these, in order to control thewater evaporation rate in low, in particular, it is preferable to usealkylated polysiloxane polyethyleneglycol copolymer.

Clay Mineral

As for a clay mineral used in the present invention, a swelling typeclay mineral and an organophilic smectite are exemplified. Examples ofthe swelling type clay mineral preferably used in the present inventioninclude, e.g., synthetic sodium magnesium silicate, lithium teniorite,sodium tetra silicate mica, lithium hectorite, and the like. As comparedwith that a conventional non-swelling type clay mineral such as naturalmica is not swelled, these swelling type clay minerals have hydrousswelling property that the clay mineral is swelled up in the case wherewater molecule is added to the middle of the crystal layer.

As for the organophilic smectite preferably used in the presentinvention, dimethyl stearyl ammonium hectorite, aluminium magnesiumsilicate processed with distearyldimethyl ammonium chloride, and thelike are listed.

Among of these clay minerals, it is preferable to use particularlysynthetic sodium magnesium silicate of the swelling type clay mineral,for the improvement of the separation stability at a high temperature.

<Hydrous Composition>

(1) Cholesterol Ester Clathrate and hydrous Composition ComprisingThereof

A cholesterol ester clathrate of the present invention is formed bystirring and mixing a HACD and a cholesterol ester.

A hydrous composition of the present invention comprising a cholesterolester clathrate and water.

The hydrous composition can be obtained by stirring and mixing acholesterol ester clathrate and water. In said hydrous composition, acholesterol ester clathrate forms micelle constitution and holds thewater content. Said hydrous composition also can be obtained by stirringand mixing a HACD, a cholesterol ester and water. FIG. 1 shows thetriangular diagram of the result of water retention lest, by usingHP-β-CD as a HACD and cholesteryl ester of macadamia nut oil fatty acidas the cholesterol ester. In 1 and 2 of the triangular diagram, thecomposition is separated into two phases, and the favorable cholesterolester clathrate cannot be obtained. On the other hand, in 3 to 6 of thetriangular diagram, the compositions become creamlike and the stablehydrous compositions are obtained. Accordingly, as for the hydrouscomposition of the present invention, preferably, the ratio of theamount of HP-β-CD and cholesteryl ester of macadamia nut oil fatty acidis existed within the range which is represented by the slant line ofFIG. 1.

(2) Hydrous Composition Comprising a Hydrous Stabilizer

A hydrous composition comprising a hydrous stabilizer of the presentinvention is composed of a HACD, water and a hydrous stabilizer, andfurther can be comprised of a hydrous oily component as additionalingredient.

In a hydrous composition of the present invention, preferably, 5 to 30%by weight of the HACD, 5 to 60% by weight of water, and 5 to 80% byweight of the hydrous oily component are compounded with respect to thewhole amount of the hydrous composition. Further, preferably, the ratioof the compounding amount of the HACD, water, and the hydrous oilycomponent is existed within the range of the triangular diagram shown inFIG. 2. In the case where the ratio of the compounding amount is notexisted within the range, it is difficult to obtain the expectedcomposition, since the separation is occurred in the middle of a waterphase and an emulsion phase.

Said hydrous composition can be obtained by dispersing the hydrousstabilizer into the hydrous oily component, adding and stirring the HACDin water solution to this, and adding and further stirring the rest ofwater to it.

(3) Hydrous Composition Comprising a Clay Mineral

A hydrous composition comprising a clay mineral of the present inventionis composed of a HACD, a cholesterol ester, a clay mineral, and water.

In a hydrous composition of the present invention, preferably, 5 to 30%by weight of the HACD, 5 to 80% by weight of the cholesterol ester, 0.01to 20% by weight of the clay mineral, and 5 to 60% by weight of waterare compounded with respect to the whole amount of the hydrouscomposition. In the case where the compounding amount is not within saidrange, the preferable emulsion phase cannot be formed. In the case wherethe compounding amount of the clay mineral is not within said range, theimprovement of the separation stability at high temperature becomeinsufficient.

Further, in the case where hydrophobic silica is compounded into saidhydrous composition, by compounding just a small amount of the claymineral, the hydrous composition which is improved the separationstability can be obtained. In particular, hydrophobic silica ispreferably compounded within the range of 0.01 to 20% by weight, and theratio of the compounding amount of hydrophobic silica to the claymineral is preferably 2:1 to 1:4.

Said hydrous composition can be obtained by dispersing the clay mineralinto the cholesterol ester and gradually adding and stirring the HACD inwater solution to this, and adding and further stirring the rest ofwater.

And, said each hydrous composition, except for said essential andselected ingredients, can be compounded the ingredients e.g., oilycomponents such as squalane; humectants such as glycerin; wax such ascandelilla wax; high polymers such as polyglyceride; medicaments such asglycyrrhizinic acid; natural surfactants such as recinol, and the like.

<Cosmetics Comprising a Hydrous Composition>

In the cosmetics of the present invention, it is possible to obtain thecosmetics which is rich in stability and safety, and is excellent inwater-holding capacity, by compounding said various hydrouscompositions. Also, the emulsion type of said hydrous composition ispreferably water-in-oil type, and in particular, it is preferable to usesaid hydrous composition as a water-in-oil cosmetics.

In this case, it is necessary to compound the hydrous composition of thepresent invention within the degree that the effects of said hydrouscomposition are sufficiently exhibited. The preferable compoundingamount of said hydrous composition is 0.5 to 30% by weight with respectto the whole amount of the cosmetics.

The cosmetics in accordance with the present invention are prepared bynormal techniques except for compounding the various hydrous compositionof the present invention which was prepared in advance.

The cosmetics in accordance with the present invention, in addition tothe hydrous composition of the present invention, can be compounded thevarious ingredients which is normally used for cosmetics within thedegree that the effects of said hydrous composition of the presentinvention are not spoiled. Examples of said various ingredients arelisted fats and oils of natural animals and vegetables such as macadamianut oil, evening primrose oil, castor oil, olive oil, mink oil, jojobaoil, lanolin, squalene and the like; wax such as liquid paraffin,paraffin wax, polyethylene wax, carnauba wax and the like; higheralcohols such as cetyl alcohol, isocetyl alcohol, stearyl alcohol,isostearyl alcohol and the like; higher fatty acids such as myristicacid, palmitic acid, stearic acid, behenic acid, isostearic acid and thelike; esters such as isopropyl myristate, isopropyl palmitate, isopropylisostearate, diisostearyl malate, trimethylolpropane triisostearate,glyceryl isostcarate, neopentyl glycol dicaprate, glyceryl2-ethylhexanoate, and the like; other oily components such as polar oils(e.g., diethylene glycol monopropylene pentaerythritol ether, ethyllinoleate, polyoxypropylene butyl ether, and the like), silicone oilsand the like; soluble powder bases such as D-mannitol, lactose and thelike; humectants such as glycerin, hyaluronic acid and the like;medicaments such as vitamin C, vitamin E and the like; antiphlogistic;UV-absorber; UV-screening agent; antioxidant; antiseptic; viscositymodifier; coloring matters; crude drugs; perfume ingredient; pigment,and the like.

The cosmetics in accordance with the present invention can be formed theconfiguration which corresponds to the various use application, e.g.,creamlike, milky lotionlike, liquidlike, solidlike, sticklike,pencillike, and the like. In the case where the cosmetics are formed theconfiguration that is particular compounded a large amounts of oil phaseingredients such as wax of solidlike, sticklike, pencillike and thelike, and that is almost never possessed water phase ingredients, thewater-holding capacity of the cosmetics can be effectively exhibited.

As for the cosmetic which uses the hydrous composition of the presentinvention, the composition for lipstick comprising a large amounts ofoil phase ingredients particular such as wax is preferable.

BRIEF DESCRIPTION OF THE DRAWINGS!

FIG. 1 is a triangular diagram which shows the ratio of the compoundingamount of a HACD, a cholesterol ester and water.

FIG. 2 is a triangular diagram which shows the ratio of the compoundingamount of a HACD, a cholesterol ester, and water, in case of compounding0.02% of a hydrous stabilizer.

FIGS. 3A to 3D are microphotographs which show the hydration propertiesof Example 1-1 (×150) (FIG. 3A), Comparative Example 1-1 (×150) (FIG.3B), Example 1-1 (×750) (FIG. 3C), and Comparative Example 1-1 (×750)(FIG. 3D).

FIGS. 4A and 4B are microphotographs which show the hydration propertiesin the after case where Example 1-1 (FIG. 4A) and Comparative Example1-1 FIG. 4B) were left for 24 hours.

FIGS. 5A and 5B are spectrum views of DSC measurement in Example 1-1(FIG. 5A) and Comparative Example 1-1 (FIG. 5B).

FIG. 6 is a chart comparing the water content of keratin in Example 1-5,Example 1-6, and Comparative example 1-3.

FIG. 7 is a chart comparing the penetrating amount of the water contentin Example 1-6, Comparative example 1-3, and Comparative example 1-4.

FIGS. 8A and 8B are spectrum views of DSC measurement in ComparativeExample 2-1 (FIG. 8A), 2-2 (FIG. 8B), and 2-3 (FIG. 8C).

FIGS. 9A and FIG. 9B are spectrum views of DSC measurement in Example2-1 (FIG. 9A) and Example 2-2 (FIG. 9B).

FIG. 10 is the results of the measurements of water evaporation ratewhich was performed by using Example 2-1 and Example 2-2.

FIGS. 11A and 11B are microphotographs which show the hydrationproperties of Example 2-3 (×300) (FIG. 11A), and Comparative Example 2-5(×300) (FIG. 11B).

FIGS. 12A and 12B are spectrum views of DSC measurement in Example 2-3(FIG. 12A) and Example 2-5 (FIG. 12B).

FIGS. 13A and 13B are spectrum views of DSC measurement in Example 3-1(FIG. 13A), Comparative Examples 3-1 (FIG. 13B) and 3-2 (FIG. 13C).

FIGS. 14A to 14D are microphotographs which show the hydrous compositionof Example 3-33 (×300) (FIG. 14A), Example 3-34 (×300) (FIG. 14B),Example 3-35 (×300) (FIG. 14C), Example 3-36 (×300) (FIG. 14D), Example3-37 (FIG. 14E), and Example 3-38 (FIG. 14F).

FIG. 15 is the results of the measurements of water evaporation ratewhich was performed by using the hydrous compositions of Example 3-33 to3-39.

BEST MODE FOR CARRYING OUT THE INVENTION!

In the following, it will be explained the present invention in furtherdetail from the embodiments of the present invention. However, thepresent invention should not be limited to the following embodiments.Also, the compounding amount is expressed as parts by weight unlessotherwise stated.

(1) Cholesterol Ester Clathrate and Hydrous Composition ComprisingThereof

In first, the inventors were studied about the physical properties ofthe cholesterol ester clathrate of the present invention. Namely,preparing the hydrous composition which comprising water and thecholesterol clathrate which included cholesteryl ester of macadamia nutoil fatty acid in hydroxypropyl β-CD (hereinafter referred to asHP-β-CD) under the following formulation. And, said composition wastaken on the preparation and was observed by microscope.

The photographs and the results obtained by the microscope observationwere shown in FIG. 3 and Table-1 respectively.

                  TABLE 1    ______________________________________                    Example 1-1                            Comp. ex. 1-1    ______________________________________    Ion-exchanged water                      40        40    HP-β-CD      10        0    cholesteryl ester of                      50        60    macadamia nut oil fatty acid    Diameter of       1 to 5    1 to 10    emulsion particle (μm)    Form of the composition                      had a visco-                                crumbly                      elasticity    ______________________________________

As is clear from the above-described results, the hydrous compositionhad a viscoelasticity, and its emulsion particle was small and also wasformed nearly spherical in Example 1-1. On the other hand, incomparative example 1-1, the composition itself showed crumbly feelingand the emulsion particle was crooked shape and was big.

Further, the microphotographs of the composition in Example 1-1 andComparative example 1-1 which were left for 24 hours, are shown in FIG.4.

As is clear from the above-described results, in Comparative example1-1, the diameter of emulsion particle became considerable big, so itcannot say that the emulsification was performed in stable. On the otherhand, in Example 1-1, the diameter of emulsion particle was considerablesmall and the particle kept the state of spherical shape, so it can saythat the emulsification was performed in stable.

Further, the inventors were performed the DSC measurement in Example 1-1and Comparative example 1-1 under the following condition.

DSC Measurement!

Measuring instrument measured by using Seiko Instruments Inc. DSC-100

Measuring condition

Rate (Heating rate): 5° C./min

Amount of the sample: 15.0 mg

Cell: Ag

Control cell: Al₂ O₃

Measured at the open condition

Temperature range: RT to 150° C.

The results of DSC measurement are shown in FIG. 5.

In comparing the result of Example 1-1 with that of Comparative example1-1, it was understood that the striking disparity was existed in theevaporation temperature of the water content. Namely, in the samplewhich removed HP-β-CD (Comparative example 1-1), the water evaporationpeak can be observed at 65° to 90° C. However, in the sample whichincluded the cholesterol ester in HP-β-CD (Example 1-1), the waterevaporation peak can be observed at the wide range of 65 to 110° C., andthe remarkable water evaporation peak further can be observed at 126° C.So, it was suggested that the composition of the present invention(Example 1-1) was possessed high water-holding capacity.

Accordingly, it was suggested that the hydrous composition of thepresent invention which comprising the cholesterol ester clathrate andwater was excellent in water-holding capacity, and was also possible toattempt the emulsification in stable.

Next, the inventors were studied about the effects in case ofcompounding the HACD.

The evaluation of emulsion stability has been done by the followingstandard.

Emulsion Stability!

∘: It was not observed the separation of the water phase and the oilphase even after kept the composition in 8 hours at 60° C.

Δ: It was observed the separation of the water phase and the emulsionphase in a part of the composition after kept the composition in 1 hourat 60° C.

X: It was observed the separation of the water phase and the oil phaseor the emulsion phase after passed 1 hour at 60° C.

                  TABLE 2    ______________________________________                Comp.                ex.   Example                1-2   1-2      1-3      1-4    ______________________________________    Cholesteryl ester of                  50      50       50     50    macadamia nut oil fatty    acid    Ion-exchanged water                  40      40       40     40    HE-β-CD  --      10       --     --    HP-β-CD  --      --       10     --    HB-β-CD  --      --       --     10    Diameter of   1 to 10 1 to 5   1 to 5 1 to 8    emulsion particle    (μm;25° C.)    Form of the composition                  crumbly had a    had a  had a                          visco-   visco- visco-                          elasticity                                   elasticity                                          elasticity    Diameter of   not     1 to 5   1 to 5 1 to 8    emulsion particle                  existed    (μm;60° C.)    Emulsion stability (60° C.)                  X       ◯                                   ◯                                          ◯    ______________________________________

As is clear from the above-described results, Comparative example 1-2which was not compounded the HACD at all, was formed emulsion particleat 25° C. However, the emulsion stability at 60° C. was bad, emulsionparticle was not formed, and the separation of the water phase and theoil phase was observed. On the other hand, all the Examples 1-2 to 1-4which were compounded the HACD, were excellent in emulsion stability at60° C., and also had a fine emulsion particle, and its form at 25° C.had a viscoelasticity. Example 1-2 and Example 1-3 which were compoundedparticularly HE-β-CD and HP-β-CD respectively, had further fine diameterof emulsion particle. So, it is preferable to use these as the HACD.

Accordingly, it is preferable to compound the HACD in the hydrouscomposition of the present invention.

Next, the inventors were compared the change of the water content ofkeratin by using the lipstick of the present invention which compoundsthe HACD, the cholesterol ester, and water (Example 1-5), the lipstickwhich compounds the hydrous composition comprising the cholesterol esterclathrate of the present invention and water (Example 1-6), the lipstickwhich was the same composition as these and was not comprising HP-β-CDand water (Comparative example 1-3).

These measurement condition is shown in the following.

Measurement of The Water Content of Keratin!

After wiped off softly the water content of lip by tissue paper in athermo-hygrostat room(22° C. and 45%), the conductance of the lip beforeputting lipstick on lip was measured. And then, putting lipstick on lip,and after passed 2 hours, wiped off the lipstick which was put on lip bytissue paper, and the conductance of the lip after put lipstick on lipwas measured. And, the ratio of the conductance before put lipstick andthe conductance after put lipstick were found.

                  TABLE 3    ______________________________________                    Comp. ex. 1-3                             Ex. 1-5 Ex. 1-6    ______________________________________    Microcrystalline wax                      1.0        1.0     1.0    Ceresin           13.5       14.5    14.5    Methylphenyl polysiloxane                      10.0       10.0    10.0    Macadamia nut oil 0.5        0.5     0.5    Glyceryl triisostearate                      18.0       18.0    18.0    Glyceryl tri(2-ethylhexanoate)                      30.67      17.03   19.66    Lanolin           5.0        5.0     5.0    Adsorption refined lanolin                      5.0        5.0     5.0    Cholesteryl ester of                      --         5.0     --    macadamia nut oil fatty acid    Dibasic calcium phosphate                      1.0        1.0     1.0    (anhydrous)    Dye               0.25       0.25    0.25    Coloring agent    15.0       15.0    15.0    Oxidation stabilizer                      0.04       0.04    0.04    Perfume           0.04       0.04    0.04    Polyoxyethylene methylpolysiloxane                      --         0.5     --    copolymer    Synthetic sodium magnesium silicate                      --         2.0     --    Ion-exchanged water                      --         4.0     --    HP-β-CD      --         1.0     --    Calcium chloride dihydrate                      --         0.13    --    Methyl polysiloxane emulsion                      --         0.01    0.01    The hydrous composition                      --         --      10.0    of Example 1-1    ______________________________________

The measurement results of the water content of keratin in case of usingthe lipstick which was obtained by Example 1-5, Example 1-6, andComparative example 1-3 are shown in FIG. 6.

As is clear from the drawing, in Example 1-5, it is suggested that theratio of the conductance was slightly big as compared with the ratio ofthe conductance of Comparative example 1-3, and it can hold the morewater content. Further, in Example 1-6, the ratio of the conductance wasmore than twice of the ratio of the conductance of Comparative example1-3, and the sufficient water content was held.

And, when the evaluation of the usability was performed by the panel byusing the lipsticks which were prepared by the above-mentionedformulation, Example 1-5 showed the characteristics such that waspossessed the moisture feeling, was excellent in spreadability andaffinity, and was less of stickiness as compared with Example 1-3.

Accordingly, in the case where the HACD, the cholesterol ester and waterwere compounded to the lipstick (Example 1-5), the lipstick which wasslightly improved the water-holding capacity and was also excellent inusability, can be obtained. Further, before mixed with lipstick bases,the hydrous composition which comprising the cholesterol ester clathratewas prepared by the HACD, water, and the cholesterol ester. In the casewhere said hydrous composition was compounded to the lipstick (Example1-6), the lipstick which had more than twice of water-holding capacityand was excellent in usability can be obtained. Accordingly, in thepresent invention, it is suggested that the moisture of the coatedsurface is keeping.

Further, the moisture effect was evaluated by measuring the penetratingamount of the water content, by using Example 1-6, Comparative example1-3, and the lipstick which is used the conventional emulsion base asthe same formulation with Example 1-6 in substitution of the hydrouscomposition of the present invention (Comparative example 1-4).

The measurement of the penetrating amount of the water content has beenperformed by coating the lipstick which was prepared by the variousformulation, on the filter paper, and by measuring the change of theamount of water content. The results are shown in FIG. 7.

In comparative example 1-3, the obtained lipstick had high blockagenature and had a little of the penetrating amount of the water content,since the lipstick was not comprised a lot of the water content.Thereupon, in case of comparing Example 1-6 with Comparative example1-3, it was shown that the penetrating amount of the water content ofExample 1-6 was less than that of Comparative example 1-3.

Accordingly, it is suggested that the hydrous composition of the presentinvention is rich in water-holding capacity, and futhermore, is stableas compared with the conventional products.

(2) Hydrous Composition Comprising a Hydrous Stabilizer

In the following, it will be explained the present invention in furtherdetail from the examples. However, the present invention should not belimited to the following examples. Also, the compounding amount isexpressed as parts by weight unless otherwise stated.

In first, the inventors were studied about the physical properties ofthe hydrous composition in accordance with the present invention.Namely, it was prepared the hydrous composition which comprisingHP-β-CD, water, and a hydrous stabilizer or a humectant under thefollowing formulation, and was studied the separation stability at hightemperature of said composition.

Separation stability!

∘: It was not observed the separation of the water phase and the oilphase even after kept the composition in 8 hours at 90° C.

Δ: It was observed the separation of the water phase and the emulsionphase in a part of the composition after kept the composition in 1 hourat 80° C.

X: It was observed the separation of the water phase and the oil phaseafter kept the composition in 1 hour at 80° C.

                  TABLE 4    ______________________________________                 Comp. ex.     Example                 2-1  2-2    2-3    2-4  2-1  2-2    ______________________________________    Cholesteryl ester of                   70     70     70   70   70   70    macadamia nut oil fatty acid    Ion-exchanged water                   20     20     20   20   20   20    HP-β-CD   0      10     10   10   10   10    Glycerin       0      0      2    0    0    0    1,3-Butylene glycol                   0      0      0    2    0    0    Alkylated polysiloxane                   0      0      0    0    2    0    polyethylene copolymer    Alkyl silicated anhydrous                   0      0      0    0    0    2    silicate    Separation stability                   X      Δ                                 Δ                                      Δ                                           ◯                                                ◯    ______________________________________

As is clear from the above-described results, in Comparative example2-1, the separation in the water phase and the oil phase was observed incase of keeping the composition in 1 hour at 80° C. Also, in Comparativeexample 2-2 to 2-4, the separation in a part of the water phase and theemulsion phase were observed in case of keeping the composition in 1hour at 80° C. On the other hand, in Example 2-1 and 2-2, the separationin the water phase and the oil phase was not observed even in case ofkeeping the composition in 8 hours at 90° C. Accordingly, it issuggested that the hydrous composition of the present invention had highseparation stability at high temperature.

Further, the inventors were performed the DSC measurement by using saidExample 2-1, Example 2-2, and Comparative examples 2-1 to 2-3 under thefollowing condition.

DSC Measurement!

Measuring instrument Seiko Instruments Inc. DSC-100

Measuring condition

Rate (Heating rate): 5° C./min

Amount of the sample: 15.0 mg

Cell: Ag

Control cell: Al₂ O₃

measured at the open condition

Temperature range: RT to 150° C.

The results of DSC measurement are shown in FIG. 8 and FIG. 9.

As is clear from FIG. 8, in Comparative example 2-1, the maximum peak ofDSC measurement was observed at 73.1° C. In Comparative example 2-2which was added HP-β-CD, the maximum peak of DSC measurement wasobserved at 83.5° C. Both Comparative examples 2-1 and 2-2 were notobserved the large peak after the maximum peak. Accordingly, it isthinkable that the water content was evaporated at 50° to 90° C. inComparative examples 2-1 and 2-2.

In Comparative example 2-3 that was compounded glycerin which was thehumectant used in general, the peak of DSC measurement was observed atin the vicinity of 80° C., and the gently curve was described even atthe temperature over the peak. So, it can gathered that the watercontent was gradually evaporated. It is thinkable that this is due tothe moisture ability of glycerin which was comprised in the composition.However, as for the water-holding at high temperature, the compositionhad a lack in stability.

On the other hand, in considering about Examples 2-1 and 2-2, each ofthe maximum peak of the DSC measurement were observed at more than 90°C. such as 106.4° C. and 94.7° C. respectively. Accordingly, it issuggested that the maximum peak of the temperature became more than 90°C. by adding the hydrous stabilizer of the present invention, and thecomposition which was improved the water-holding capacity at hightemperature can be obtained.

Further, the inventors were studied about the water evaporation rate ofsaid Examples 2-1 and 2-2.

The results are shown in FIG. 10.

As is clear from the drawing, in comparing with the results of Examples2-1 and 2-2, the water evaporation rate of Example 2-1 was less thanthat of Example 2-2, the disparity was widened with passage of time.Namely, it was cleared that the side which was compounded alkylatedpolysiloxane polyethyleneglycol copolymer had low water evaporation ratein case of keeping in a long period of time and at high temperature.

Next, Example 2-3 and Comparative example 2-5 which removed HP-β-CD fromthe formulation of Example 2-3, were prepared as shown in the followingformulation. And the compositions were taken on the preparation and wereobserved by microscope. And, DSC measurement was performed under thesame condition as the above-described condition. In Example 2-3 andComparative example 2-5, squalane was compounded for adjusting theviscosity.

The microphotographs which were obtained by microscope observation areshown in FIG. 11. The results are shown in Table-4 together with itsformulation. Also, the results of DSC measurement are shown in FIG. 12.

                  TABLE 5    ______________________________________                    Example 2-3                            Comp. ex. 2-5    ______________________________________    Cholesteryl ester of                      70        70    macadamia nut oil fatty acid    Ion-exchanged water                      20        20    HP-β-CD      10        0    Alkylated polysiloxane                      2         2    polyethylene copolymer    Squalane (adjusting viscosity)                      20        20    Diameter of       1 to 3    not    emulsion particle (μm)   existed    Form of the composition                      creamlike ununiformity                      in uniformly                                (separation into                                two phases)    ______________________________________

As is clear from the above-described results and microphotographs, inExample 2-3 which was compounded HP-1 -CD, the emulsion particle whoseform was uniform creamlike and whose particle diameter was 1 to 3 μm,was existed. And it is thinkable that the emulsification was performedin stable. On the other hand, in Comparative example 2-5 which removedHP-β-CD from Example 2-3, the emulsion particle was not existed and thecomposition was separated into the oil phase and the water phase,therefore the emulsification cannot performed in stable.

Next, in case of comparing the results of DSC measurement in FIG. 12, itwas understood that the striking disparity of water evaporationtemperature was existed between Example 2-3 and Comparative example 2-5.Namely, in Comparative example 2-5 which removed HP-β-CD from Example2-3, the peak of water evaporation temperature was observed at 70° to100° C. On the other hand, in Example 2-3 which compounded HP-β-CD, thepeak of water evaporation temperature was observed at a range between100° to 130° C. From these results, it is suggested that the compositionof the present invention had the high water-holding capacity even underthe severe circumstance more than 90° C.

Further, the inventors were studied about the effects of the compoundingof the HACD.

                  TABLE 6    ______________________________________                  Comp. ex.                         Example                  2-6    2-4     2-5     2-6    ______________________________________    Cholesteryl ester of                    70       70      70    70    macadamia nut oil fatty acid    Ion-exchanged water                    20       20      20    20    HE-β-CD    --       10      --    --    HP-β-CD    --       --      10    --    HB-β-CD    --       --      --    10    Alkylated polysiloxane                    2        2       2     2    polyethylene copolymer    Diameter of     not      1 to 3  1 to 3                                           1 to 3    emulsion particle (μm)                    existed    Form of the composition                    separation                             cream   cream cream                             like    like  like    ______________________________________

As is clear from the above-described results, in Comparative example 2-6which was not compounded the HACD, the emulsion particle cannot beformed and the composition was separated into the water phase and theoil phase. On the other hand, in Example 2-4 to 2-6 which compounded theHACD, the emulsion particle were formed the small sphere whose diameterwere 1 to 3 μm, and the excellent composition which is creamlike can beobtained.

Further, the inventors were prepared the lipstick (Example 2-7) whichcompounded the composition of Example 2-1, and the lipstick (Comparativeexample 2-7) which directly compounded the same amount as Example 2-1 ofHP-β-CD, water, cholesteryl ester of macadamia nut oil fatty acid, andalkylated polysiloxane polyethylene copolymer. And, the visualobservation (aggregation of coloring agent), change of the water contentof keratin, and the penetrating amount of the water content, werecompared by using these lipsticks which were prepared as above forevaluating the hydration properties at the time of the products wereformed. These various lipsticks were prepared by the following process.The composition of the various lipsticks are shown in Table-7 togetherwith the results of visual observation.

(Process 1; Example 2-7)

The hydrous composition was prepared in advance (cf. Example 2-1). Thehydrous composition was added to the lipstick bases which were dissolvedat 80° C. After stirred it 10 minutes by disper stirring, the obtainedcomposition was kept in 5 minutes at 90° C.

(Process 2; Comparative example 2-7)

The lipstick bases were dissolved at 80° C. And after added anddissolved cholesteryl ester of macadamia nut oil fatty acid andalkylated polysiloxane polyethylene copolymer to it, adding the solutionof HP-β-CD which was dissolved into water, to the oil phase, stirring it10 minutes by disper stirring. And, the obtained composition was kept in5 minutes at 90° C.

                  TABLE 7    ______________________________________                   Comp. ex. 2-7                             Example 2-7    ______________________________________    A.  Lipstick bases        Carnauba wax     0.5          0.5        Candelilla wax   5.0          5.0        Ceresin          10.0         10.0        Squalane         11.0         11.0        Liquid paraffin  30.0         30.0        Glyceryl isostearate                         14.8         14.8        Glyceryl diisostearate                         8.3          8.3    B.  Hydrous composition        Hydrous composition                         --           20.4        of Example 2-1        HP-β-CD     2.0          --        Cholesteryl ester of                         14.0         --        macadamia nut oil fatty acid        Alkylated polysiloxane                         0.4          --        polyethylene copolymer        Ion-exchanged water                         4.0          --        Visual Observation;                         ununiformity by                                      the emulsion                         separated into the                                      particle was                         oil phase and the                                      uniformly                         emulsion phase                                      dispersed    ______________________________________

As is clear from the above-described results, as shown in Comparativeexample 2-7, in the case where the various ingredients of the hydrouscomposition were separately compounded, the obtained composition becameununiform by the separation into the oil phase and the emulsion phase,and had lack in the separation stability. In the case where the variousingredients were added separately to the composition, water was adsorbedto alkylated polysiloxane polyethylene copolymer used in the presentinvention as the hydrous stabilizer. And, silicone is inferior incompatibility with respect to the hydrocarbon type oily component. So,it is thinkable that the composition was separated into the emulsionphase of silicone active agent and the oil phase of hydrocarbon.

On the other hand, in Example 2-7 which comprising the hydrouscomposition of the present invention, the hydrous composition wasuniformly dispersed. It is thought that the emulsion particle isconsiderably fine and has high dispersibility as shown in Example 2-3.

Accordingly, the hydrous composition of the present invention has highseparation stability and can he favorably kept the water phase into theoil phase.

(3) Hydrous Composition Comprising a Clay Mineral

In first, the inventors paid attention to a clay mineral as thematerials which improved the separation stability. And, they preparedthe hydrous composition by the formulation of the following Table-8, andstudied about the physical properties of the hydrous composition of thepresent invention. And, it has been studied by using HP-β-CD as theHACD, cholesteryl ester of macadamia nut oil fatty acid as thecholesterol ester, and synthetic sodium magnesium as the clay mineral.The following composition is shown as parts by weight.

Separation Stability at High Temperature!

∘: It was not observed the separation of the water phase and the oilphase even after kept the composition 8 hours at 90° C.

Δ: It was observed the separation of the water phase and the emulsionphase in a part of the composition after kept the composition in 1 hourat 80° C.

X: It was observed the separation of the water phase and the oil phaseor the emulsion phase after passed 1 hour at 80° C.

                  TABLE 8    ______________________________________              Comp. ex. 3-1                       Comp. ex. 3-2                                  Example 3-1    ______________________________________    Cholesteryl ester of                60         60         60    macadamia nut oil    fatty acid    Ion-exchanged water                40         40         40    HP-β-CD                0          10         10    Synthetic sodium                0          0          5    magnesium silicate    Diameter of 1-10       1-5        --    emulsion particle (μm)    Form of the crumbly    had a      had a    composition            visco-     visco-                           elasticity elasticity    Separation stability                X          Δ    ◯    ______________________________________

As is clear from the above-described results, Comparative example 3-1which was obtained by mixing the cholesterol ester and water, becamecrumbly itself, and had a large emulsion particle, and it was observedthe separation into the water phase and the oil phase at hightemperature. And also, Comparative example 3-2 which compounded HP-β-CDto Comparative example 3-1, had small diameter of emulsion particle andhad a viscoelasticity. However, in case of keeping the composition athigh temperature, it was observed the separation of the water phase andthe emulsion phase in a part of the composition. On the other hand, inExample 3-1, the emulsion particle of sphere shape cannot observed.However the excellent hydrous composition which had a viscoelasticityand had a high separation stability even at high temperature can beobtained.

Further, the inventors were performed the DSC measurement about theExample 3-1, Comparative example 3-1, and 3-2 by the followingcondition. The results are shown in FIG. 13.

DSC Measurement!

Measuring instrument Seiko Instruments Inc DSC-100

Measuring condition

Rate (Heating rate): 5° C./min

Amount of the sample: 15.0 mg

Cell: Ag

Control cell: Al₂ O₃

measured at the open condition

Temperature range: RT to 150° C.

As is clear from the drawings, in Comparative example 3-1, the maximumpeak was 73.1° C. and was lower than that of Comparative example 3-2 andExample 3-1.

The maximum peak of Comparative example 3-2 and Example 3-1 were 83.5°C. and 82.4° C. respectively, and were almost equivalent. However, inExample 3-1, the peak were observed at 103.6° C. and 128° C., and theevaporation of the water content can be observed even more than 100° C.It was thought as the peak of water which is held in stable, sincesynthetic sodium magnesium silicate take water into the middle of thephases.

Accordingly, from the physical properties of the composition and theresults of DSC measurement, it is suggested that the composition inaccordance with the present invention is the composition which has highseparation stability and is also excellent in water-holding.

Next, the inventors were studied about the effects of the compounding ofthe hydroxyalkylated cyclodextrin.

                  TABLE 9    ______________________________________               Comp. ex.                      Example               3-3    3-2      3-3      3-4    ______________________________________    Cholesteryl ester of                 68       68       68     68    macadamia nut oil    fatty acid    Ion-exchanged water                 20       20       20     20    HP-β-CD --       10       --     --    HE-β-CD --       --       10     --    HB-β-CD --       --       --     10    Synthetic sodium                 5        5        5      5    magnesium silicate    Diameter of  --       --       --     --    emulsion particle (μm)    Form of the  separation                          had a    had a  had a    hydrous composition   visco-   visco- visco-                          elasticity                                   elasticity                                          elasticity    Separation stability                 X        ◯                                   ◯                                          ◯    ______________________________________

As is clear from the above-described results, in Comparative example 3-3which was not compounded the HACD at all, the separation of the waterphase and the oil phase at high temperature was observed. On the otherhand, in Examples 3-2 to 3-4 which were compounded HP-β-CD, HE-β-CD, andHB-β-CD respectively, each of the composition had a viscoelasticity, andbecame excellent in the separation stability at high temperature.

Accordingly, it is suggested that the composition which is favorablyimproved the separation stability can be obtained, by compounding thehydroxyalkylated cyclodextrin.

Next, the inventors were studied about the relationships between thecompounding amount of the clay mineral and separation stability of thehydrous composition at high temperature.

                  TABLE 10    ______________________________________                 Example                 3-5  3-6    3-7    3-8  3-9  3-10    ______________________________________    Cholesteryl ester of                   68     68     68   68   68   68    macadamia nut oil fatty acid    Squalane       20     20     20   20   20   20    Synthetic sodium                   0      1      3    5    10   20    magnesium silicate    HP-β-CD   10     10     10   10   10   10    Glycerin       2      2      2    2    2    2    Water          20     20     20   20   20   20    Separation stability                   X      Δ                                 Δ                                      ◯                                           ◯                                                ◯    ______________________________________

As is clear from the above-described results, in the condition which wasnot compounded synthetic sodium magnesium silicate, the separationstability at high temperature is bad, and the separation of the waterphase and the oil phase or the emulsion phase was confirmed. Also, inthe case where 1 to 3 parts by weight of synthetic sodium magnesiumsilicate were compounded, though the stability were improved, theimprovement was not sufficient. On the other hand, in the case where 5to 20 parts by weight of synthetic sodium magnesium silicate werecompounded, separation stability at high temperature were improved.

Next, the inventors were prepared the hydrous composition under thefollowing formulation by using other clay minerals, and were studiedabout the emulsion stability.

                  TABLE 11    ______________________________________                  Example                  3-11  3-12   3-13   3-14 3-15    ______________________________________    Cholesteryl ester of                    68      68     68   68   68    macadamia nut oil fatty acid    Squalane        20      20     20   20   20    Lithium teniorite                    5       --     --   --   --    Sodium tetra silicate mica                    --      5      --   --   --    Lithium hectorite                    --      --     5    --   --    Mica            --      --     --   5    --    Dimethyl stearyl                    --      --     --   --   5    ammonium hectorite    HP-β-CD    10      10     10   10   10    Glycerin        2       2      2    2    2    Water           20      20     20   20   20    Separation stability                    ◯                            ◯                                   ◯                                        Δ                                             ◯    ______________________________________

From the above-described results, in case of using lithium tennessee,sodium tetra silicate mica, lithium hectorite which were the swellingtype clay mineral as like synthetic sodium magnesium silicate, theseparation stability were improved, as like the case used syntheticsodium magnesium silicate. And, in case of compounding dimethylstearylammonium hectorite which was the organophilic smectite, the improvementof separation stability can be observed.

On the other hand, in case of compounding mica which was thenon-swelling type clay mineral, separation stability was improved in apart, but the sufficient stability cannot be obtained.

Next, the inventors were studied about the compounding of hydrophobicsilica for improving the separation stability by compounding a littleamount of the clay mineral and for obtaining a further fine emulsionparticle, since the clay minerals were caused the surface roughness andwere worsened the feeling of use in some time. The diameter of emulsionparticle was observed by using light microscope. The evaluation wasstudied about separation stability at high temperature and water-holdingcapacity.

Water-Holding Capacity!

∘: Water evaporation rate after passed 8 hours at 90° C. was less than20%

X: Water evaporation rate after passed 8 hours at 90° C. was 20% or more

                  TABLE 12    ______________________________________              Example              3-16 3-17   3-18   3-19 3-20 3-21 3-22    ______________________________________    Cholesteryl ester of                68     68     68   68   68   68   68    macadamia nut oil    fatty acid    Squalane    20     20     20   20   20   20   20    Hydrophobic silica                2      2      2    2    2    2    2    Synthetic sodium                3      --     --   --   --   --   --    magnesium silicate    Lithium teniorite                --     3      --   --   --   --   --    Sodium tetra                --     --     3    --   --   --   --    silicate mica    Lithium hectorite                --     --     --   3    --   --   --    Mica        --     --     --   --   3    --   --    Dimethyl stearyl                --     --     --   --   --   3    --    ammonium hectorite    Aluminium magnes-                --     --     --   --   --   --   3    ium silicate processed    with distearyldimethyl    ammonium chloride    HP-β-CD                10     10     10   10   10   10   10    Glycerin    2      2      2    2    2    2    2    Water       20     20     20   20   20   20   20    Diameter of 1 to 8 1 to 8 1 to 8                                   1 to 8                                        3 to 1 to 3                                                  1 to 3    emulsion particle (μm)           20    Separation stability                ◯                       ◯                              ◯                                   ◯                                        ◯                                             ◯                                                  ◯    Water-holding                ◯                       ◯                              ◯                                   ◯                                        ◯                                             ◯                                                  ◯    capacity    ______________________________________

As is clear from the above-described results, in the case wherehydrophobic silica and the clay mineral were compounded with combining,the improvement of separation stability at 90° C. can be observed in allclay minerals. And, in the case where 3 parts by weight of syntheticsodium magnesium silicate was compounded in separately, the separationstability at high temperature was not sufficient (in Table-7, Example3-4). However, in the case where hydrophobic silica was compounded, thesufficient separation stability can be obtained. Also, since thecompounding amount of the clay mineral was small, it was not caused theproblems in the feeling of use such as surface roughness.

Further, when the inventors measured the diameter of emulsion particleof each composition by using light microscope, the fine emulsionparticle whose diameter were 1 to 8 μm were observed in the swellingtype clay mineral and the organophilic smectite. On the other hand, inmica which is the non-swelling type clay mineral, the considerable largeemulsion particle whose diameter was 3-20 μm was formed.

Accordingly, in the case where hydrophobic silica was compounded, theseparation stability at high temperature was improved and the excellenthydrous composition which had fine emulsion particle was also formed, bycompounding just a small amount of clay mineral.

Next, by using HE-β-CD, HP-β-CD and HB-β-CD, the study were performedabout the properties of the composition which were compounded withhydrophobic silica. In this place, synthetic sodium magnesium silicatewas used as the clay mineral.

                  TABLE 13    ______________________________________                 Ex. 3-23                         Ex. 3-24  Ex. 3-25    ______________________________________    Cholesteryl ester of                   68        68        68    macadamia nut oil fatty acid    Squalane       20        20        20    Hydrophobic silica                   2         2         2    Synthetic sodium                   5         5         5    magnesium silicate    HE-β-CD   10        --        --    HP-β-CD   --        10        --    HB-β-CD   --        --        10    Glycerin       2         2         2    Water          20        20        20    Diameter of    2 to 8    2 to 8    2 to 8    emulsion particle (μm)    Separation stability                   ◯                             ◯                                       ◯    Form of the composition                   had a     had a     had a                   visco-    visco-    visco-                   elasticity                             elasticity                                       elasticity    ______________________________________

As is clear from the above-described results, in the case wherehydrophobic silica was combined with any one of said HACD, the emulsionparticle which had a viscoelasticity and fine particle diameter can beformed. In particular, it was more preferable to compound with HE-β-CDor HP-β-CD, since the fine emulsion particle was formed.

Next, the inventors were studied about the compounding amount ofhydrophobic silica. In this place, synthetic sodium magnesium silicatewas used as the clay mineral.

                  TABLE 14    ______________________________________              Example              3-26 3-27   3-28   3-29 3-30 3-31 3-32    ______________________________________    Cholesteryl ester of                68     68     68   68   68   68   68    macadamia nut oil    fatty acid    Squalane    20     20     20   20   20   20   20    Hydrophobic silica                0      0.01   1    5    10   20   25    Synthetic sodium                3       3     3    3    3    3    3    magnesiuin silicate    HP-β-CD                10     10     10   10   10   10   10    Glycerin    2       2     2    2    2    2    2    Water       20     20     20   20   20   20   20    Compounding amount                0      0.016  0.8  3.9  7.5  14.0 19.6    of hydrophobic silica    (% by weight)    Diameter of --     3 to   2 to 1 to 2                                        to 1 to 1 to 1    emulsion particle (μm)                       30     15    Separation stability                Δ                       ◯                              ◯                                   ◯                                        ◯                                             ◯                                                  ◯    ______________________________________

As is clear from the above-described results, in the case wherehydrophobic silica was not compounded at all, the separation stabilitywas not improved, and the emulsion particle cannot observed. On theother hand, in the case where more than 20% by weight of hydrophobicsilica were compounded, the improvement of the separation stability canbe observed. However, the compounding amount of silica became large inrelative, it sometimes worsened the feeling of use of the composition.

Accordingly, it is preferable to compound hydrophobic silica within arange of 0.01 to 20% by weight.

Next, the study was performed about the ratio of the compounding amountof hydrophobic silica and the clay mineral in the case where hydrophobicsilica and the clay mineral were used by combining together.

In this place, synthetic sodium magnesium silicate was used as the claymineral.

                  TABLE 15    ______________________________________              Example              3-33 3-34   3-35   3-36 3-37 3-38 3-39    ______________________________________    Cholesteryl ester of                68     68     68   68   68   68   68    macadamia nut oil    fatty acid    Squalane    20     20     20   20   20   20   20    Hydrophobic silica                2      2      2    2    2    2    2    Synthetic sodium                0      1      3    5    7    10   20    magnesium silicate    HP-β-CD                10     10     10   10   10   10   10    Glycerin    2      2      2    2    2    2    2    Water       20     20     20   20   20   20   20    Diameter of 3 to   2 to   2 to 8                                   2 to 8                                        1 to 5                                             --   --    emulsion particle (μm)                20     15    Separation stability                ◯                       ◯                              ◯                                   ◯                                        ◯                                             ◯                                                  ◯    ______________________________________

As is clear from the above-described results, in the case wherehydrophobic silica was compounded, the excellent separation stabilitycan be obtained in all the hydrous composition. Also, in measuring thediameter of emulsion particle, in the case where synthetic sodiummagnesium silicate was not compounded, it was formed the emulsionparticle whose diameter was 3 to 20 μm, and the fine emulsion particlewas not formed (Example 3-33 and FIG. 14A). Also, in the case where morethan 10 parts by weight of synthetic sodium magnesium silicate wascompounded, though the separation of the water phase and the emulsionphase was not observed, the emulsion particle cannot be observed(Example 3-39 and FIG. 14F). On the other hand, in the case where 1 to 7parts by weight of synthetic sodium magnesium silicate were compounded,it can formed the fine emulsion particle whose diameter was 1 to 15 μm(Example 3-34 to 3-37, FIG. 14B to E).

Also, FIG. 15 is the results of the study of the water evaporation rateby using the above-described Example 3-33 to 3-39. As is clear from FIG.15, the water evaporation rate was inhibited by compounding syntheticsodium magnesium silicate. Accordingly, it is suggested that thewater-holding capacity was improved by the addition of clay mineral.

Accordingly, in the case where hydrophobic silica and the clay mineralwere compounded by combining together, the ratio of the compoundingamount of hydrophobic silica to the clay mineral was preferably 2:1 to1:4.

Further, it will be shown the more concrete compounding examples of thepresent invention.

(1) Compounding Examples Used a Hydrous Composition Comprising aCholesterol Ester Clathrate

Each of the compounding examples had a large conductance ratio of thewater content of keratin, and were excellent in water-holding capacityand keeping stability, and had no apprehension about the irritation forskin.

    ______________________________________    Compounding example 1-1 Skin lotion    ______________________________________    A. Water phase part    Glycerin               10.0% by weight    Propylene glycol        5.0    Ethanol                 5.0    Parahydroxybenzoic acid ester                            0.2    Purified water         residue    B. Hydrous composition    HP-β-CD            0.4    Cholesterol ester (Olive oil fatty acid)                            0.1    Purified water          0.5    C. Oil phase part    Cetyl isooctanoate      4.0    2-Ethylhexyl 4-methoxycinnamate                            0.1    ______________________________________

(Process)

Adding the solution of HP-β-CD which was dissolved into 0.1% by weightof purified water to the cholesterol ester of 60° C., and stirring it 10minutes by a disper. And then, adding the rest of purified water (0.4%by weight) to it and stirring it 10 minutes by a homomixer, and thehydrous composition was prepared. After adding this hydrous compositionto the water phase part, adding the oil phase part to it and stirring it10 minutes by a homomixer, and the skin lotion was obtained.

    ______________________________________    Compounding example 1-2 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax           0.5 parts by weight    Candelilla wax         5.0    Ceresin               10.0    Squalane              30.0    Glyceryl triisostearate                          10.0    Glyceryl diisostearate                          20.0    B. Hydrous composition    HP-β-CD           1.0    Cholesterol ester (Isostearic acid)                           3.5    Glycerin               0.5    Purified water         2.0    C. Other bases    Coloring agent        q.s.    Perfume               q.s.    Antiseptic            q.s.    ______________________________________

(Process)

Adding the solution of HP-β-CD which was dissolved into 0.5 parts byweight of purified water to the cholesterol ester of 60° C., andstirring it 10 minutes by a disper. And then, adding the rest ofpurified water (1.5 parts by weight) and glycerin to it and stirring it10 minutes by a homomixer, and the hydrous composition was prepared. Thelipstick bases were dissolved at 80° C., and the hydrous composition wasadded to this. After stirring it 10 minutes by a disper, adding coloringagent, perfume, and antiseptic to it, dispersing and stirring it, thenthe lipstick was formed.

    ______________________________________    Compounding example 1-3 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax          0.5 parts by weight    Candelilla wax        5.0    Ceresin              10.0    Squalane             30.0    Glyceryl triisostearate                         10.0    Glyceryl diisostearate                         20.0    B. Hydrous composition    HP-β-CD          1.0    Cholesterol ester (Oleic acid)                          3.5    Glycerin              0.5    Purified water        2.0    C. Other bases    Coloring agent       q.s.    Perfume              q.s.    Antiseptic           q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example1-2.

    ______________________________________    Compounding example 1-4 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax           0.5 parts by weight    Candelilla wax         5.0    Ceresin               10.0    Squalane              30.0    Glyceryl triisostearate                          10.0    Glyceryl diisostearate                          20.0    B. Hydrous composition    HF-β-CD           1.0    Cholesterol ester (Isostearic acid)                           4.0    Glycerin               0.5    Purified water         1.5    C. Other bases    Coloring agent        q.s.    Perfume               q.s.    Antiseptic            q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example1-2.

    ______________________________________    Compounding example 1-5 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax          0.5 parts by weight    Candelilla wax        5.0    Ceresin              10.0    Squalane             30.0    Glyceryl triisostearate                         10.0    Glyceryl diisostearate                         20.0    B. Hydrous composition    HE-β-CD          1.0    Cholesterol ester (Oleic acid)                          4.0    Glycerin              0.5    Purified water        1.5    C. Other bases    Coloring agent       q.s.    Perfume              q.s.    Antiseptic           q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example1-2.

    ______________________________________    Compounding example 1-6 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax             0.5 parts by weight    Candelilla wax           5.0    Ceresin                 10.0    Squalane                30.0    Glyceryl triisostearate 10.0    Glyceryl diisostearate  20.0    B. Hydrous composition    HP-β-CD             1.0    Cholesteryl ester of macadamia nut oil fatty acid                             3.5    Glycerin                 0.2    Purified water           2.0    C. Other bases    Coloring agent          q.s.    Perfume                 q.s.    Antiseptic              q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example1-2.

(2) Hydrous composition comprising a hydrous stabilizer

Each of the compounding examples had a large conductance ratio of thewater content of keratin, and were excellent in water-holding capacityand keeping stability, and had no apprehension about the irritation forskin.

    ______________________________________    Compounding example 2-1 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax            0.5 parts by weight    Candelilla wax          5.0    Ceresin                10.0    Squalane               30.0    Glyceryl triisostearate                           10.0    Glyceryl diisostearrate                           20.0    B. Hydrous composition    HP-β-CD            1.0    Cholesterol ester (Isostearic acid)                            3.5    Alkylated polysiloxane polyethylene copolymer                            0.2    Glycerin                0.5    Purified water          1.0    C. Other bases    Coloring agent         q.s.    Perfume                q.s.    Antiseptic             q.s.    ______________________________________

(Process)

Dispersing alkylated polysiloxane polyethylene copolymer as the hydrousstabilizer into the cholesterol ester of 60° C., and adding the solutionof HP-β-CD which was dissolved into 0.5 parts by weight of purifiedwater to it, and stirring it 10 minutes by a disper. And then, addingthe rest of purified water (1.5 parts by weight) and glycerin to it andstirring it 10 minutes by a homomixer, and the hydrous composition wasprepared. The hydrous composition was added to the lipstick bases whichwere dissolved at 80° C. After stirring it 10 minutes by a disper,adding coloring agent, perfume, and antiseptic to it and dispersing andstirring it. And then, forming it and the lipstick was obtained.

    ______________________________________    Compounding example 2-2 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax           0.5 parts by weight    Candelilla wax         5.0    Ceresin               10.0    Squalane              30.0    Glyceryl triisostearate                          10.0    Glyceryl diisostearate                          20.0    B. Hydrous composition    HP-β-CD           1.0    Cholesterol ester (Oleic acid)                           3.5    Alkyl silicated anhydrous silicate                           0.2    Glycerin               0.5    Purified water         1.0    C. Other bases    Coloring agent        q.s.    Perfume               q.s.    Antiseptic            q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example2-1.

    ______________________________________    Compounding example 2-3 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax             0.5 parts by weight    Caridelilla wax          5.0    Ceresin                 10.0    Squalane                30.0    Glyceryl triisostearate 10.0    Glyceryl diisostearate  20.0    B. Hydrous composition    HP-β-CD             1.0    Cholesterol ester (Stearic acid)                             3.5    Glyceryl-modified silicone resin coated powder                             0.2    Glycerin                 0.5    Purified water           2.0    C. Other bases    Coloring agent          q.s.    Perfume                 q.s.    Antiseptic              q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example2-1.

    ______________________________________    Compounding example 2-4 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax          0.5 parts by weight    Caridelilla wax       5.0    Ceresin              10.0    Squalane             30.0    Glyceryl triisostearate                         10.0    Glyceryl diisostearate                         20.0    B. Hydrous composition    HP-β-CD          1.0    Cholesterol ester (Oleic acid)                          3.5    Dextrin fatty acid ester                          0.2    Glycerin              0.5    Purified water        1.5    Coloring agent       q.s.    Perfume              q.s.    Antiseptic           q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example2-1.

    ______________________________________    Compounding example 2-5 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax            0.5 parts by weight    Candelilla wax          5.0    Ceresin                10.0    Squalane               30.0    Glyceryl triisostearate                           10.0    Glyceryl diisostearate 20.0    B. Hydrous composition    HE-β-CD            1.0    Cholesterol ester (Oleic acid)                            3.5    Alkylated polysiloxane polyethylene copolymer                            0.2    Glycerin                0.5    Purified water          1.5    C. Other bases    Coloring agent         q.s.    Perfume                q.s.    Antiseptic             q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example2-1.

    ______________________________________    Compounding example 2-6 Lipstick    ______________________________________    A. Lipstick bases    Carnauba wax             0.5 parts by weight    Candelilla wax           5.0    Ceresin                 10.0    Squalane                30.0    Glyceryl triisostearate 10.0    Glyceryl diisostearate  20.0    B. Hydrous composition    HB-β-CD             1.0    Cholesteryl ester of macadamia nut oil fatty acid                             3.5    Alkyl silicated anhydrous silicate                             0.2    Glycerin                 0.5    Purified water           1.5    C. Other bases    Coloring agent          q.s.    Perfume                 q.s.    Antiseptic              q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example2-1.

    ______________________________________    Compounding example 2-7 Lipstick    ______________________________________    A.  Lipstick bases        Carnauba wax            0.5 parts by weight        Candelilla wax          5.0        Ceresin                 10.0        Squalane                30.0        Glyceryl triisostearate 10.0        Glyceryl diisostearate  20.0    B.  Hydrous composition        HP-β-CD            1.0        Cholesterol ester (Oleic acid)                                3.5        Squalane                2.0        Alkylated polysiloxane polyethylene copolymer                                0.2        Glycerin                0.5        Purified water          1.5    C.  Other bases        Coloring agent          q.s.        Perfume                 q.s.        Antiseptic              q.s.    ______________________________________

(Process)

After compounding squalane into the cholesterol ester of 60° C. foradjusting the viscosity, dispersing alkylated polysiloxane polyethylenecopolymer as the hydrous stabilizer into the cholesterol ester of 60°C., and adding the solution of HP-β-CD which was dissolved into 0.5% byweight of water to it, and stirring it 10 minutes by a disper. And then,adding the rest of purified water (1.5% by weight) and glycerin to itand stirring it 10 minutes by a homomixer, and the hydrous compositionwas prepared. The lipstick bases were dissolved at 80° C., and thehydrous composition was added to this. And, after stirring it 10 minutesby a disper, adding coloring agent, perfume, and antiseptic to it,dispersing and stirring it. And then, forming it and the lipstick wasobtained.

    ______________________________________    Compounding example 2-8 Cream    ______________________________________    A.  Oil phase        Microcrystalline wax    8.0 parts by weight        Solid paraffin          2.0        Beeswax                 3.0        Petrolatum              6.0        Hydrogenated lanolin    5.0        Squalane                30.0        Hexadecyl adipate ester 8.0        Glyceryl monooleate     3.5        POE(20) sorbitol monooleate ester                                1.0    B.  Other bases        Coloring agent          q.s.        Perfume                 q.s.        Antiseptic              q.s.    C.  Water phase        Purified water          15.0        Propylene glycol        5.0    D.  Hydrous composition        HP-β-CD            1.0        Cholesteryl ester of macadamia nut oil fatty                                3.5        acid        Squalane                2.0        Alkylated polysiloxane polyethylene copolymer                                0.2        Glycerin                1.5        Puried water            1.5    ______________________________________

(Process)

After compounding squalane into cholesteryl ester of macadamia nut oilfatty acid of 60° C. for adjusting the viscosity, alkylated polysiloxanepolyethylene copolymer as the hydrous stabilizer was dispersed into it.Adding the solution of HP-β-CD which was dissolved into 0.5 parts byweight of purified water to it, and stirred it 10 minutes by a disper.And then, adding ther rest of purified water (1.5 parts by weight) andglycerin to it and stirring it 10 minutes by a homomixer, and thehydrous composition was prepared.

After heating and dissolving the oil phase, preparing it at 70° C. byadding antiseptic agent, antioxidant, and perfume to it. Preparing byadding propylene glycol to purified water at 70° C. (water phase). Thewater phase was gradually added into the oil phase which was prepared inadvance. After emulsifying by stirring it 10 minutes by a homomixer,adding the hydrous composition which was prepared by the above-mentionedprocess to it. After further stirring it 10 minutes by a homomixer, thecream was obtained by deaerating and cooling it.

(3) Hydrous composition comprising a clay mineral

Each of the compounding examples showed favorable separation stabilityat high temperature, and the compounding examples itself were excellentin water-holding capacity, and it became the excellent composition whichhad no apprehension about irritation for skin.

    ______________________________________    Compounding example 3-1 Lipstick    ______________________________________    A.  Lipstick bases        Carnauba wax            0.5 parts by weight        Candelilla wax          5.0        Ceresin                 10.0        Squalane                30.0        Glyceryl triisostearate 10.0        Glyceryl diisostearate  20.0    B.  Hydrous composition        HP-β-CD            1.0        Cholesterol ester (Isostearic acid)                                3.5        Synthetic sodium magnesium silicate                                2.0        Glycerin                0.5        Water                   1.0    C.  Other bases        Coloring agent          q.s.        Perfume                 q.s.        Antiseptic              q.s.    ______________________________________

(Process)

Dispersing alkylated polysiloxane polyethylene copolymer as the hydrousstabilizer into the cholesterol ester of 60° C., and adding the solutionof HP-β-CD which was dissolved into 0.5% by weight of water to it, andstirring it 10 minutes by a disper. And then, adding the rest of waterand glycerin to it and stirring it 10 minutes by a homomixer, and thehydrous composition was prepared. The hydrous composition was added tothe lipstick bases which were dissolved at 80° C. And, after stirring it10 minutes by a disper, adding coloring agent, perfume, and antisepticto it, and dispersing and stirring it. And then, forming it and thelipstick was obtained.

    ______________________________________    Compounding example 3-2 Lipstick    ______________________________________    A.  Lipstick bases        Carnauba wax            0.5 parts by weight        Candelilla wax          5.0        Ceresin                 10.0        Squalane                30.0        Glyceryl triisostearate 10.0        Glyceryl diisostearate  20.0    B.  Hydrous composition        HP-β-CD            1.0        Cholesterol ester (Oleic acid)                                3.5        Squalane                2.0        Sodium tetra silicate mica                                0.5        Glycerin                1.0        Water                   1.0    C.  Other bases        Coloring agent          q.s.        Perfume                 q.s.        Antiseptic              q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example3-1.

    ______________________________________    Compounding example 3-3 Lipstick    ______________________________________    A.    Lipstick bases          Carnauba wax     0.5 parts by weight          Candelilla wax   5.0          Ceresin          10.0          Squalane         30.0          Glyceryl triisostearate                           10.0          Glyceryl diisostearate                           20.0    B.    Hydrous composition          HP-β-CD     1.0          Cholesterol ester (Oleic acid)                           3.5          Squalane         2.0          Sodium tetra silicate mica                           0.5          Hydrophobic silica                           0.5          Glycerin         1.0          Water            1.0    C.    Other bases          Coloring agent   q.s.          Perfume          q.s.          Antiseptic       q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example3-1.

    ______________________________________    Compounding example 3-4 Lipstick    ______________________________________    A.    Lipstick bases          Carnauba wax     0.5 parts by weight          Candelilla wax   5.0          Ceresin          10.0          Squalane         30.0          Glyceryl triisostearate                           10.0          Glyceryl diisostearate                           20.0    B.    Hydrous composition          HE-β-CD     1.0          Cholesterol ester (Oleic acid)                           3.5          Sodium tetra silicate mica                           0.5          Glycerin         0.5          Water            1.5    C.    Other bases          Coloring agent   q.s.          Perfume          q.s.          Antiseptic       q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example3-1.

    ______________________________________    Compounding example 3-5 Lipstick    ______________________________________    A.  Lipstick bases        Carnauba wax            0.5 parts by weight        Candelilla wax          5.0        Ceresin                 10.0        Squalane                30.0        Glyceryl triisostearate 10.0        Glyceryl diisostearate  20.0    B.  Hydrous composition        HB-β-CD            1.0        Cholesteryl ester of macadamia nut oil fatty                                3.5        acid        Synthetic sodium magnesium silicate                                0.5        Hydrophobic silica      0.5        Glycerin                0.2        Water                   2.0    C.  Other bases        Coloring agent          q.s.        Perfume                 q.s.        Antiseptic              q.s.    ______________________________________

(Process)

The lipstick was obtained by the same process with Compounding example3-1.

    ______________________________________    Compounding example 3-6 Cream    ______________________________________    A.  Oil phase        Microcrystalline wax    8.0 parts by weight        Solid paraffin          2.0        Beeswax                 3.0        Petrolatum              6.0        Hydrogenated lanolin    5.0        Squalane                30.0        Hexadexyl adipate ester 3.0        Glyceryl monooleate     3.5        POE (20) sorbitol monooleate ester                                1.0    B.  Other bases        Antiseptic              q.s.        Antioxidant             q.s.        Perfume                 q.s.    C.  Water phase        Purified water          15.0        Propylene glycol        5.0    D.  Hydrate composition        HP-β-CD            1.0        Cholesteryl ester of macadamia nut oil fatty                                3.5        acid        Squalane                2.0        Synthetic sodium magnesium silicate                                0.5        Glycerin                1.5        Purified water          1.5    ______________________________________

(Process)

After compounding squalane into cholesteryl ester of macadamia nut oilfatty acid of 60° C. for adjusting the viscosity, dispersing syntheticsodium magnesium silicate into it, and adding the solution of HP-β-CDwhich was dissolved into the purified water to it, and stirring it 10minutes by a disper. And then, the hydrous composition was prepared.

After heating and dissolving the oil phase, preparing it at 70° C. byadding antiseptic agent, antioxidant, and perfume to it. Preparing byadding propylene glycol to water at 70° C. (water phase). The waterphase was gradually added into the oil phase which was prepared inadvance, after emulsifying by stirring it 10 minutes by a homomixer,adding the hydrous composition which was prepared by the above-mentionedprocess, to it. After further stirring it 10 minutes by a homomixer, thecream was obtained by deaerating and cooling it.

We claim:
 1. A hydrous composition comprising:5 to 30% by weight of ahydroxyalkylated cyclodextrin, 0.01 to 20% by weight of a hydrousstabilizer, wherein said hydrous stabilizer is at least one selectedfrom the group consisting of alkylated polysiloxane polyethyleneglycolcopolymer, alkyl silicated anhydrous silicate, alkyl-modified siliconeresin coated powder, glyceryl-modified silicone resin coated powder, anddextrin fatty acid ester, 5 to 60% by weight of water, and 5 to 80% byweight of an oily component with respect to the whole amount of thehydrous composition.
 2. A hydrous composition according to claim 1,wherein relative proportions of the hydroxyalkylated cyclodextrin,water, and the oily component are determined by coordinates along aslant line of a triangular diagram shown in FIG.
 2. 3. A hydrouscomposition comprising:5 to 30% by weight of a hydroxyalkylatedcyclodextrin, 5 to 80% by weight of a cholesterol ester, 0.01 to 20% byweight of a clay mineral, wherein said clay mineral is a swelling claymineral or an organophilic smectite, 0.01 to 20% by weight of ahydrophobic silica, and 5 to 60% by weight of water with respect to thewhole amount of the hydrous composition.
 4. A hydrous compositionaccording to claim 3, wherein said swelling clay mineral is a syntheticsodium magnesium silicate.
 5. A hydrous composition according to claim3, wherein the ratio of the compounding amount of hydrophobic silica tothe clay mineral is 2:1 to 1:4.
 6. A process for making a hydrouscomposition comprising:stirring and mixing 5 to 30% by weight of ahydroxyalkylated cyclodextrin, 5to 60% by weight of water, 0.01 to 20%by weight of a hydrous stabilizer, wherein said hydrous stabilizer is atleast one selected from the group consisting of alkylated polysiloxanepolyethyleneglycol copolymer, alkyl silicated anhydrous silicate,alkyl-modified silicone resin coated powder, glyceryl-modified siliconeresin coated powder, and dextrin fatty acid ester, and 5 to 80% byweight of an oily component.
 7. A process for making the hydrouscomposition according to claim 6, wherein relative proportions of thehydroxyalkylated cyclodextrin, water, and the oily component aredetermined by coordinates along a slant line of a triangular diagramshown in FIG.
 2. 8. A process for making a hydrous compositioncomprising:stirring and mixing 5 to 30% by weight of a hydroxyalkylatedcyclodextrin, 5 to 80% by weight of a cholesterol ester, 0.01% to 20% byweight of a clay mineral, wherein said clay mineral is a swelling claymaterial or an organophilic smectite, 0.01 to 20% by weight of ahydrophobic silica, and 5to 60% by weight of water.
 9. A process formaking the hydrous composition according to claim 8, wherein saidswelling clay mineral is a synthetic sodium magnesium silicate.
 10. Aprocess for making the hydrous composition according to claim 8 or 9,wherein the ratio of the compounding amount of hydrophobic silica to theclay mineral is 2:1 to 1:4.
 11. A process of making a cosmeticcomprising:mixing and stirring 5 to 30% by weight of a hydroxyalkylatedcyclodextrin, 5 to 60% by weight of water, 0.0l to 20% by weight of ahydrous stabilizer, wherein said hydrous stabilizer is at least oneselected from the group consisting of alkylated polysiloxanepolyethyleneglycol copolymer, alkyl silicated anhydrous silicate,alkyl-modified silicone resin coated powder, glyceryl-modified siliconeresin coated powder, and dextrin fatty acid ester, and 5 to 80% byweight of an oily component to form a hydrous composition, and mixingand stirring said hydrous composition with at least one cosmeticingredient selected from the group consisting of macadamia nut oil,evening primrose oil, castor oil, olive oil, mink oil, jojoba oil,lanolin, squalene, liquid paraffin, paraffin wax, polyethylene wax,carnauba wax, cetyl alcohol, isocetyl alcohol, stearyl alcohol,isostearyl alcohol, myristic acid, palmitate, stearate, behenic acid,isostearate, diisostearyl malate, trimethylolpropane triisostearate,glyceryl isostearate, neopentyl glycol dicaprate, glyceryl2-ethylhexanoate, diethylene glycol monopropylene pentaerythritol ether,ethyl linoleate, polyoxypropylene butyl ether, silicon oil, D-mannitol,lactose, glycerin, hyaluronic acid, vitamin C, vitamin E, perfume, andpigment.
 12. A process of making a cosmetic comprising the stepsof:mixing and stirring 5 to 30% by weight of a hydroxyalkylatedcyclodextrin, 5 to 80% by weight of a cholesterol ester, 0.01% to 20% byweight of a clay mineral, wherein said clay mineral is a swelling claymaterial or an organophilic smectite, 0.01 to 20% by weight of ahydrophobic silica, and 5 to 60% by weight of water to form a hydrouscomposition, and mixing and stirring said hydrous composition with atleast one cosmetic ingredient selected from the group consisting ofmacadamia nut oil, evening primrose oil, castor oil, olive oil, minkoil, jojoba oil, lanolin, squalene, liquid paraffin, paraffin wax,polyethylene wax, carnauba wax, cetyl alcohol, isocetyl alcohol, stearylalcohol, isostearyl alcohol, myristic acid, palmitate, stearate, behenicacid, isostearate, diisostearyl malate, trimethylolpropanetriisostearate, glyceryl isostearate, neopentyl glycol dicaprate,glyceryl 2-ethylhexanoate, diethylene glycol monopropylenepentaerythritol ether, ethyl linoleate, polyoxypropylene butyl ether,silicon oil, D-mannitol, lactose, glycerin, hyaluronic acid, vitamin C,vitamin E, perfume ingredient, and pigment.
 13. The process for making acosmetic according to claim 11, wherein 0.5 to 30% by weight of saidhydrous composition is compounded with respect to a whole amount of saidcosmetic.
 14. The process for making a cosmetic according to claim 12,wherein 0.5 to 30% by weight of said hydrous composition is compoundedwith respect to a whole amount of said cosmetic.